Photochromic Technology
WeeTect Photochromic Technology (WPT) includes two types of photochromic technologies. Once of them is photochromic coating. The substrate is injection molded polycarbonate lenses, polycarbonate visors or polycarbonate face shields. Then we use special photochromic material to do photochromic coating on the surface. Another photochromic technology is photochromic co-mold. We firstly perform the special photochromic film or photochromic sheet. Then we will process co-injection molding with the photochromic film to produce photochromic lenses or photochromic goggles. WeeTect Photochromic Technology (WPT) can be applied to make all kinds of photochromic lenses, photochromic sunglasses, transition lenses, photochromic goggles, photochromic lenses, photochromic visor, photochromic face shield, and more.
WeeTect Photochromic Technology (WPT) is one of the best photochromic technologies with an optical clarify on photochromic clear situation, and turns to photochromic tint quickly under UV radiation. In advance, WeeTect Photochromic Technology (WPT) can combine other surface treatments such as anti-fog coating, anti-scratch coating, iridium coating and more. As an eye and face protection solution provider, WeeTect holds the know-how of photochromic coating and co-mold photochromic technology. We are glad to co-develop other special photochromic applications for niche market.
Photochromic Technology Review of Advantages:
- Convenience: One piece of photochromic lenses, photochromic visor or photochromic face shield can fulfill varying light conditions.
- UV protection: WeeTect Photochromic Technology (WPT)absorbs 100% UV harmful radiation.
- One stop solution: WeeTect Photochromic Technology (WPT)also combines anti-fog coating, hard coating, abrasion resistant coating, iridium coating or other color tinting together.
- Reduce cost: As a capable photochromic lens manufacturer, WeeTect can support you to reduce cost.
PS: Here is a photochromic ebook for you to learn more about photochromic technology
- Gallery
- Data Sheet
- Video
- Contact us Now
| Item | Property | Test Method | U/M | Value |
| Optical | UV Resistant | EN170 | % | 99.99% |
| Haze | ASTM D 1003 | % | 0.37 | |
| VLT Before Photochromic Tint | ASTM D 1003 | % | 87 | |
| VLT Fully Photochromic Tint | ASTM D 1003 | % | 20 | |
| Fully Photochromic Tint Time | WeeTect Method | Second | 30 | |
| Change Back to Photochromic Clear Time | WeeTect Method | Minutes | 3 | |
| Fog Free time | ECE22.05/ECE324 | s | >22 | |
| Fog Free time | Freezing Test | s | no fogging | |
| Mechanical | Hardness 1KG | ISO 178 | H | 1 |
| High velocity impact | ANSI Z87.1 2010 | ft/s | >300 | |
| Cross-Cut tape test | ASTM D 1000 | NA | Pass | |
| Elongation, yield % 7 | ISO 527 | % | 7 | |
| Elongation, break ISO 527 % 110 | ISO 527 | % | 110 | |
| Tensile stress, yield | ISO 527 | Mpa | 60 | |
| Tensile modulus MPa | ISO 527 | Mpa | 2300 | |
| Flexural strength, yield | ISO 178 | Mpa | 100 | |
| Flexural modulus ISO 178 MPa 2500 | ISO 178 | Mpa | 2500 | |
| Izod notched impact, 20 °C | ISO 180-1A | KJ/m² | 65 | |
| Physical | Gravity | ISO 1183 | g/cm³ | 1.2 |
| Water absorption, 24 hours | ISO 62 | % | 0.15 | |
| Thermal | Mold shrinkage | ISO527 | % | 0.5-0.7 |
| Thermal expansion | ASTM D696 | 1/ °C | 7×10-5 | |
| Vicat Softening Temp., Rate B / 120(base sheet) | ISO 306 | °C | 150 | |
| HDT, 0.45 MPa | ISO 75/Be | °C | 138 |