Anti Scratch Coating
WeeTect Anti Scratch Coating (WASC) also name scratch resistant coating which is a spraying or dipping technology for plastic sheet coating, film coating and injection molding visors optical class 1 in clean coating room. It is one of the best anti scratch solutions. WeeTect Anti Scratch Coating (WASC) can be used for scratch resistant safety glasses, anti fog anti scratch safety glasses, scratch resistant acrylic sheet, polycarbonate coating, other scratch resistant plastic and more.
WeeTect Anti Scratch Coating (WASC) offers excellent performance on anti scratch properties as well as optical clarity. Compared with the other anti-scratch coating suppliers, WeeTect Anti Scratch Coating (WASC) has better abrasion resistance. At the same time, WeeTect also offer custom solution for any applications require scratch resistant properties.
Advantages of WeeTect Anti Scratch Coating:
- Better scratch resistant features
- Better optical visibility
- High end dipping and spraying processes
- Much more cost competitive
- More custom flexible
- Anti-fog coating as an option
Applications of WeeTect Anti Scratch Coating:
- Anti-scratch window films indoor and outdoor use
- Anti-scratch plastic lenses which are applied to control platforms
- Anti-scratch films or polycarbonate sheets which are applied to LCD or LED panels
- Anti-scratch coating on injected LED panels or LED shells
- Gallery
- Technical Data
- Standard Product
| Item | Property | Test Method | U/M | Value |
| Optical | Diopter | ECE 22.05 | D | <0.125 |
| Haze | ASTM D 1003 | % | 0.37 | |
| Mechanical | Hardness 1KG | ANSI Z87.1 2010 | H | 1 |
| High velocity impact | ANSI Z87.1 2010 | ft/s | >300 | |
| Cross-Cut tape test | ISO 527 | NA | Pass | |
| Elongation, yield % 7 | ISO 527 | % | 7 | |
| Elongation, break ISO 527 % 110 | ISO 527 | % | 110 | |
| Tensile stress, yield | ISO 527 | Mpa | 60 | |
| Tensile modulus MPa | ISO 527 | Mpa | 2300 | |
| Flexural strength, yield | ISO 178 | Mpa | 100 | |
| Flexural modulus ISO 178 MPa 2500 | ISO 178 | Mpa | 2500 | |
| Izod notched impact, 20 °C | ANSI Z87.1 2010 | KJ/m² | 65 | |
| Physical | Gravity | ISO 1183 | g/cm³ | 1.2 |
| Water absorption, 24 hours | ANSI Z87.1 2010 | % | 0.15 | |
| Thermal | Mold shrinkage | ISO 11359 | % | 0.5-0.7 |
| Thermal expansion | ISO 11357 | 1/ °C | 7×10-5 | |
| Vicat Softening Temp., Rate B / 120(base sheet) | ASTM D5470 | °C | 150 | |
| HDT, 0.45 MPa | ISO 11357 | °C | 138 |
| Thickness (mm) | Width (mm) | Length (mm) | Remark |
| 0.125 | 930 | 400,000 | Optical Grade |
| 0.15 | 930 | 350,000 | Optical Grade |
| 0.25 | 930 | 300,000 | Optical Grade |
| 0.3 | 930 | 300,000 | Optical Grade |
| 0.5 | 930 | 160,000 | Optical Grade |
| 0.5 | 915 | 1,830 | Optical Grade |
| 0.6 | 915 | 1,830 | Optical Grade |
| 0.7 | 915 | 1,830 | Optical Grade |
| 0.8 | 915 | 1,830 | Optical Grade |
| 1 | 915 | 1,830 | Optical Grade |
| 1.5 | 1,220 | 1,830 | Optical Grade |
| 2 | 1,220 | 1,830 | Optical Grade |
| 3 | 1,220 | 1,830 | Optical Grade |
| 4 | 1,220 | 1,830 | Optical Grade |
| 6 | 1,220 | 1,830 | Clear |
| 8 | 1,220 | 1,830 | Clear |