WeePro® Anti-fog Visor Insert
WeePro® Anti-fog Visor Insert (WAFVI) also names helmet visor film which is one of anti-fog inserts used for anti-fog visor. It is made from anti-fog film with circled back adhesive. WeePro® Anti-fog Visor Insert (WAFVI) is an excellent and cost competitive anti-fog solution for motorcycle visor anti-fog, football visor inserts and other helmet visors inserts. WeePro® is glad to custom the anti-fog visor inserts with your own design.
WeePro® Anti-fog Visor Insert (WAFVI) offer superior anti-fog performance to motorcycle helmet visor manufacturers, branding company, distributors, dealers and wholesalers. Compare with Pinlock anti-fog visor insert and fog city anti-fog visor insert, WeePro® Anti-fog Visor Insert (WAFVI) has comparable performance but much more competitive cost. Having a sustainable performance increases the longevity of the product and reduces significant costs; WeePro® Anti-fog Visor Insert (WAFVI) can be easily applied to all types of helmet visor inserts.
Advantages:
- Universal version fits for most helmet visors
- Better optical clarity with lower distortion
- Better fog resistant feature
- More abrasion resistant
- Much more cost competitive
- More custom flexible
- Video
- Installation Guide
- Review
- Image Gallery
- Technical Data
Technical Data of WeeTect Anti fog visor inserts
Item | Property | Test Method | U/M | Value |
Optical | Diopter | ECE 22.05 | D | <0.125 |
Haze | ASTM D 1003 | % | 0.37 | |
Fog Free time | ECE22.05/ECE324 | s | >22 | |
Fog Free time | Freezing Test | s | no fogging | |
Mechanical | Hardness 1KG | ISO 178 | H | 1 |
High velocity impact | ANSI Z87.1 2010 | ft/s | >300 | |
Cross-Cut tape test | ISO 527 | NA | Pass | |
Elongation, yield % 7 | ISO 527 | % | 7 | |
Elongation, break ISO 527 % 110 | ISO 527 | % | 110 | |
Tensile stress, yield | ISO 527 | Mpa | 60 | |
Tensile modulus MPa | ISO 527 | Mpa | 2300 | |
Flexural strength, yield | ISO 178 | Mpa | 100 | |
Flexural modulus ISO 178 MPa 2500 | ISO 178 | Mpa | 2500 | |
Izod notched impact, 20 °C | ANSI Z87.1 2010 | KJ/m² | 65 | |
Physical | Gravity | ISO 1183 | g/cm³ | 1.2 |
Water absorption, 24 hours | ANSI Z87.1 2010 | % | 0.15 | |
Thermal | Mold shrinkage | ISO 11359 | % | 0.5-0.7 |
Thermal expansion | ISO 11357 | 1/ °C | 7×10-5 | |
Vicat Softening Temp., Rate B / 120(base sheet) | ASTM D5470 | °C | 150 | |
HDT, 0.45 MPa | ISO 11357 | °C | 138 |