Security Window Film
WeeTect Security Window Film (WSWF) also names window security film which is a coated polycarbonate or polyester film with permanent anti-scratch properties on the outer layer and a back adhesive on the inner layer. It is an explosion proof film to keep window safety by high impact resistant and super good back adhesive.
WeeTect Security Window Film (WSWF) offers excellent impact resistance, optical clarity, and anti-scratch performance. It is an easy and economical way to keep clients exist glass panel but improve the impact resistance and superior protection on anti-terrorism proposition.
With superior performance for manufacturers or companies in security window film, WeeTect Security Window Film (WSWF) excels in abrasion and impact resistance. With a long life guaranteed, WeeTect helps your business reduce significant costs. WeeTect Security Window Film (WSWF) is applicable to all specialized buildings such as: jewelry shops, museums, counters, residences and more.
- Gallery
- Technical Data
- Standard Product
| Item | Property | Test Method | U/M | Value |
| Optical | Haze | ASTM D 1003 | % | 0.37 |
| Mechanical | Hardness 1KG | ISO 178 | H | 1 |
| High velocity impact | ANSI Z87.1 2010 | ft/s | >300 | |
| Cross-Cut tape test | ISO 527 | NA | Pass | |
| Elongation, yield % 7 | ISO 527 | % | 7 | |
| Elongation, break ISO 527 % 110 | ISO 527 | % | 110 | |
| Tensile stress, yield | ISO 527 | Mpa | 60 | |
| Tensile modulus MPa | ISO 527 | Mpa | 2300 | |
| Flexural strength, yield | ISO 178 | Mpa | 100 | |
| Flexural modulus ISO 178 MPa 2500 | ISO 178 | Mpa | 2500 | |
| Izod notched impact, 20 °C | ANSI Z87.1 2010 | KJ/m² | 65 | |
| Physical | Gravity | ISO 1183 | g/cm³ | 1.2 |
| Water absorption, 24 hours | ANSI Z87.1 2010 | % | 0.15 | |
| Thermal | Mold shrinkage | ISO 11359 | % | 0.5-0.7 |
| Thermal expansion | ISO 11357 | 1/ °C | 7×10-5 | |
| Vicat Softening Temp., Rate B / 120(base sheet) | ASTM D5470 | °C | 150 | |
| HDT, 0.45 MPa | ISO 11357 | °C | 138 |
| Property | 2 mil | 4 mil | 8 mil |
| Durability of Adhesive Strength (ibs/s*s) | 7,224.80 | 20,213.60 | 32,181.60 |
| Average Breaking Strength (PSI) | 21,344.00 | 20,140.50 | 23,939.50 |
| Elongation (%) | 143.70% | 134% | 130% |
| Visible Light Transmission (VLT, %) | 93.21% | 93.05% | 91.18% |
| UV Resistant Rate (%) | 56.84% | 55.53% | 47.58% |
| IR Resistant Rate (%) | 75.37% | 75.67% | 75.67% |
| Thickness (mm) | Width (mm) | Length (mm) | Remark |
| 0.125 | 930 | 400,000 | Optical Grade |
| 0.15 | 930 | 350,000 | Optical Grade |
| 0.175 | 930 | 350,000 | Optical Grade |
| 0.25 | 930 | 300,000 | Optical Grade |
| 0.3 | 930 | 300,000 | Optical Grade |
| 0.5 | 930 | 160,000 | Optical Grade |